Thank you for visiting nature.com. You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.
Scientific Reports volume 13, Article number: 12075 (2023 ) Cite this article Tinox Titanium Dioxide
This study focused on a direct comparison of conventional hydrothermal and microwave treatment during the synthesis of TiO2–Fe3O4 photocatalyst, which is an effective catalyst for decomposing metronidazole. The photocatalyst underwent various characterization analyses, including X-ray diffraction, Raman spectroscopy, transmission electron microscopy, energy dispersive X-ray, and diffuse reflectance spectroscopy. The Raman spectroscopy analysis revealed that the materials obtained through the conventional hydrothermal treatment consisted of separate phases of anatase and magnetite. On the other hand, the materials synthesized using the microwave process showed a noticeable shift in the Eg band (143 cm−1) and its half-width towards higher wavenumbers. This shift is likely due to the introduction of Fe ions into the TiO2 lattice. Additionally, both conventional hydrothermal and microwave synthesis routes produced TiO2–Fe3O4 systems with superparamagnetic properties, as demonstrated by SQUID magnetic measurements. The TEM analysis revealed that the materials synthesized using the microwave process exhibited higher homogeneity, with no noticeable large aggregates observed. Finally, this work proposed a convenient LED photoreactor that effectively utilized the photo-oxidative properties of TiO2–Fe3O4 photocatalysts to remove metronidazole. Combining photoactive TiO2–Fe3O4 catalysts with an energy-efficient LED reactor resulted in a low electrical energy per order (EEO).
In the current global situation, it is extremely important to care for the natural environment in the pursuit of climate neutrality. This objective is at the heart of the European Green Deal1,2, which has been accepted by all countries in the European Union. However, it is also crucial to skillfully use available energy resources. Now more than ever, the world sees that changing our energy strategy will achieve climate neutrality and ensure peace of mind in the world’s electricity markets. Additionally, researchers are constantly challenged to consider more environmentally friendly methods for the fabrication of desired products3. Among the guiding principles of green chemistry, the desire to use safer solvents and design for energy efficiency are two key principles relevant to materials science4.
Titanium dioxide is one of the most extensively studied powder materials in materials science, with nearly 200,000 results in the Scopus database (access date May 10, 2023). Its popularity can be attributed to its excellent photocatalytic properties, which make it suitable for the photooxidation of organic pollutants. However, the use of titanium dioxide in industrial wastewater treatment is limited due to certain drawbacks5,6. One such limitation is the difficulty in separating TiO2 from the post-process mixture. Another is the high rate of recombination of electron/hole charge carriers, which reduces process efficiency over time7. This affects the overall process performance and requires significant investments in TiO2 suspension separation to recover the photocatalyst for reuse in subsequent processes. One possible strategy to address the challenges of titanium dioxide photocatalysts is to incorporate a component that can improve material separation after the process8,9. Magnetite (Fe3O4), which is a mixture of two iron oxides has ferromagnetic properties due to the unbalanced magnetic contributions of FeII and FeIII electrons10. The combination of the properties of both oxides allows for the production of magnetic photocatalysts for use in the photodegradation of organic pollutants. For instance, Chu et al.11 synthesized a stable core–shell TiO2@Fe3O4 system based on carbon, which exhibited enhanced photocatalytic capabilities. Similarly, Guo et al.12 developed a TiO2/Fe3O4/graphene material with increased activity for the removal of methylene blue. However, selecting an appropriate synthesis method that preserves both the photooxidative capacity and magnetic properties of the final system remains a major challenge for researchers13.
Currently, one of the most popular processes in materials science is the sol–gel technique, which is based on the hydrolysis reaction of organometallic precursors in the reaction mixture14. However, one of the main disadvantages of this process is the need for additional heat treatment at high temperatures, which requires significant amounts of electricity15. Additionally, the process generates off-gases that contribute to the carbon footprint16,17. Another popular process is the hydrothermal method, which simulates the growth of crystals during the mineralization process in nature18. This process is based on conventional heating, which heats the walls of the reactor and then the reactants by convection or conduction19. The reactor acts as an intermediary for the transfer of thermal energy from an external heat source, and this path typically leads to thermal gradients in the bulk media and to inefficient and heterogeneous reactions. Moreover, the undoubted disadvantages of the hydrothermal method include high equipment requirements, long reaction time, and high energy consumption20,21. However, taking into account the mild conditions of hydrothermal processes, pioneering work of changing the heating mechanism by including microwaves was carried out by Komarneni and Roy22. The authors reported that microwave heating involves two main mechanisms, dipolar polarization, and ionic conduction. Hence, microwaves heat any material containing mobile electric charges, such as polar molecules or conducting ions in a solvent or in a solid. Due to the high rate constant of the process, the microwave process can sometimes lead to overheating of the reaction mixture, which can lead to unwanted side reactions23. Moreover, the lack of precise temperature control can result in the formation of non-uniform products24. Despite this, microwave heating is indicated as an alternative heat source for rapid volumetric heating with a shorter reaction time and higher reaction rate. However, it seems that in the case of microwave-assisted processes, other effects occur in addition to shortening the processing time. Among others, Jiang et al.25 indicate the effect of microwave irradiation on nucleation relative to crystal growth. In addition, available scientific reports indicate that microwave radiation determines molecular processes due to differences in the absorption of microwave energy by compounds in the reaction mixture, which causes local temperature changes26,27,28. In another study, Teixeira et al.5 synthesized Na2Ti6O13 nanoparticles using the hydrothermal synthesis method with a lower concentration of NaOH under soft conditions. It is worth paying attention to the work presented by Gedye et al.29, who indicate the influence of many factors, such as sample volume, solvent, homogeneous and heterogeneous reactions, reaction vessel size, and power level on microwave-assisted processes. However, until today, the detailed mechanism of the chemical reaction under microwave irradiation has still not been fully understood30,31. Zhu and Cheng32 indicate that in many cases, reports on the specific microwave effects were based on inaccurate comparisons of microwave heating with conventional heating. Therefore, the authors reported that a large number of carefully designed comparative studies between microwave heating and conventional heating are necessary for further understanding of microwave heating mechanisms.
To meet the actual expectations, this paper compares the synthesis of TiO2–Fe3O4 photocatalyst using conventional hydrothermal and microwave treatment to meet current expectations. The novelty of this study is demonstrated by the different mechanisms used to produce the systems. The materials created through the microwave process exhibited a shift in the Eg band towards higher wavenumbers due to the introduction of Fe ions into the TiO2 lattice. Additionally, the study proposed an LED photoreactor that effectively utilized the photo-oxidative properties of TiO2–Fe3O4 photocatalysts to remove metronidazole, resulting in a low electrical energy per order (EEO). The improvement in photoactivity is attributed to the formation of a heterojunction between the TiO2 and Fe3O4 components of the system.
TiCl4 (97%), FeCl2·4H2O (98%), FeCl3·6H2O (97%) NH3·H2O (25%), PEG400 (p.a.), ammonium oxalate (99%), silver nitrate (>99%), tert-butyl alcohol (99%) benzoquinone (p.a.) and metronidazole (>99%) were purchased from Sigma-Aldrich (USA). The used reagents had an analytical grade. Whereas the water used in all experiments was deionized.
The synthesis of the TiO2–Fe3O4 systems was realized using the conventional hydrothermal and microwave routes. In the first stage, titanium(IV) chloride solution (1 wt%) was prepared in distilled water in an ice-water bath according to the procedure previously reported elsewhere33. The TiCl4 solution was then placed in an IKA reactor (Ika Werke GmBH, Germany) and stirred at 100 rpm. A 25% ammonia solution was then added with constant stirring until pH 9. The resulting suspension was transferred to a hydrothermal reactor (Parr Instrument Co., USA) or a microwave reactor (CEM Discover SPD 80, USA) and subjected to heat treatment. The heat treatment parameters were: for the hydrothermal process—T = 200 °C, t = 12 h, for the microwave treatment—T = 200 °C, t = 5 min, P = 300W. After the process was completed, the reactor was cooled to room temperature and the obtained material was washed three times with deionized water. Then it was dried at 60 °C for 6 h.
The procedure for obtaining TiO2–Fe3O4 systems was started by placing 50 mL of the mixture of Fe3O4 precursors in the ratio of Fe2+:Fe3+ = 1:1.5 (0.1 g:0.2 g) ions and a 0.1 g of polyethylene glycol in the IKA reactor (Ika Werke GmBH, Germany). Then, 3 mL of ammonia water solution was added to the reaction mixture, and the system was stirred at 1000 rpm. Subsequently, a specified amount of TiO2 suspension (see Table S1 in the Supplementary Materials) was added to the resulting mixture and homogenized for 30 min. The resulting reaction mixture was then subjected to hydrothermal microwave treatment. The heat treatment parameters were: conventional hydrothermal—T = 200 °C, t = 12 h, microwave treatment—T = 200 °C, t = 5 min, P = 300W. The resulting materials were separated using an external magnetic field and washed until a clear liquid was obtained over the layer of the system. The washed precipitate was dried at 45 °C for 12 h. Each of the synthesized samples series was described according to the following formula:
where Method abbreviation—M in case the microwave processing; H—for conventional hydrothermal treatment. X%—the amount of magnetite (wt% Fe3O4 = 2.5%; 5%; 10%; 15% or 20%).
The X-ray diffraction analysis was performed using a Rigaku Miniflex 600 diffractometer (Rigaku, Japan). The measurement was conducted using CuKα radiation (λ = 1.5406 Å) in the range of 2θ = 20°–80° at a scan speed of 1°/min. The International Center for Diffraction Data (ICDD) database was used to interpret the obtained diffractions. Quantitative analysis of the phase composition, including the standard deviation, was performed using the reference intensity ratio method with the most intense independent peak of each phase. The crystallite size of the analyzed materials was determined using the Scherrer equation (Eq. 2)34,35:
where D—average crystallite size (nm); K—Scherrer constant (0.891); λ—X-ray wavelength (λ = 1.5406 Å); β—line broadening at half the maximum intensity (FWHM), θ—Bragg angle (degree).
Raman spectra were performed using the Renishaw micro-Raman system from inVia. The spectra were recorded in the spectral range of 100–1600 cm−1, in the backscattering geometry by the confocal. The excitation light of 488 nm was used by a tunable Ar-ion laser. Renishaw WiRE 3.4 software was used for data collection and deconvolution of the obtained spectra.
The morphology and microstructure of the obtained systems were determined using the Hitachi HT7700 transmission electron microscope (TEM) operating in high contrast and high-resolution mode. The maps of selected elements of the synthesized materials were generated using the same TEM (HT 7700) operating in scanning transmission electron microscopy (STEM) mode, equipped with the EDS X-ray microanalysis system from Thermo Scientific (USA).
The textural properties of surface area, pore volume, and pore diameter were determined using the low-temperature nitrogen sorption method. The ASAP 2020 porosimeter from Micromeritics Instrument Co. in Norcross, USA was used for the analysis. Prior to measurement, the materials were degassed at 120 °C for 4 h. The surface area was determined using the multipoint BET method by analyzing adsorption data in a relative pressure (p/p0) range of 0.05–0.30.
Magnetic measurements were carried out using the Quantum Design MPMS-XL SQUID magnetometer (USA). The temperature dependence of magnetization was measured in a magnetic field of 0.1 T over the temperature range of 2–300 K. Magnetization loops were collected at both 5 K and 300 K in magnetic fields up to 5 T.
Diffuse reflectance spectroscopy (DRS) was used to measure the light absorption properties of all obtained oxide materials. The measurements were conducted using a Thermo Scientific Evolution 220 spectrophotometer (Waltham, USA) equipped with a PIN-757 integrating sphere, and BaSO4 was used as a reference. The bandgap energy of the obtained samples was calculated from the plot of (F(R)·E)0.5 against E, where E is the photon energy, and F(R) is the Kubelka–Munk function proportional to the absorption of radiation.
The photoluminescence (PL) measurements were carried out using a spectrofluorometer (Fluorolog version-3 Horiba, Japan) with a 450 W high-pressure xenon arc lamp as an excitation source. The photoluminescence excitation (λ = 330 nm) and emission spectra were acquired at room temperature at a spectral resolution of 2 nm at a slit width of 2 mm.
The Jupiter STA 449 F3 apparatus (Netzsch GmbH, Bad Berneck im Fichtelgebirge, Germany) was used to determine thermogravimetric curves. The analysis were performed under flowing nitrogen at a heating rate of 10 °C/min in a temperature range of 30–1000 °C.
Initially, a solution of metronidazole (20 mg L−1) was prepared in a volume of 1 L and mixed with 1 g of photocatalyst in the photoreactor. Exactly the same amount of metronidazole solution (1 L) was used for each experiment. To prevent the influence of indoor light, the process was conducted in a black box. The resulting mixture was homogenized in darkness for 30 min to establish adsorption/desorption equilibrium. Afterward, the UV-LED lamp was switched on, and the reaction mixture was irradiated. The detailed characteristics of the LED light source used are presented in Supplementary Materials. At intervals of 20 min (up to 180 min, after which the irradiation was stopped), 3 mL of the suspension was collected and filtered through a syringe filter (Macherey–Nagel, Germany). The filtered solution was analyzed using a UV–Vis spectrophotometer (UV 2020, Shimadzu, Japan) in the wavelength range of 200–700 nm, using the spectrum of demineralized water as the baseline. The maximum absorbance of pollution was observed at a wavenumber of 315 nm. The photocatalytic activity of the samples was determined by applying the calibration curve method, which had the formula y = 0.028x − 0.009, where x was the metronidazole concentration and y was the maximum absorbance value. The investigation aimed to comprehend how charge carriers and reactive oxygen species participate in the photocatalytic reaction, providing insights into the mechanism behind the degradation of organic contaminants when using the synthesized photocatalysts. To evaluate the photocatalytic activity, the procedure described above was followed, but with the inclusion of scavenger solutions in appropriate amounts. The concentrations of these scavenger solutions were adjusted to achieve a level of 20 mg/dm3 for metronidazole. Specifically, ammonium oxalate was selected as the scavenger for holes (h+), AgNO3 for electrons (e-), tert-butyl alcohol for free hydroxyl radicals (*OH), and benzoquinone for superoxide radical anions (*O2–).
The X-ray diffraction patterns of TiO2–Fe3O4 systems synthesized by conventional and microwave treatment are shown in Fig. 1. To determine the structural properties of the samples, Rietveld analysis was conducted using FullProf software, and the results for selected systems are presented in Fig. S1 of the Supplementary Materials. The phase composition and average crystallite size for the synthesized materials are summarized in Table S2 in Supplementary Materials. The black curves in the figure represent the typical XRD pattern of anatase36,37. The TiO2 reference materials obtained a similar crystallite size of 18.1 nm, regardless of the treatment method used (conventional hydrothermal or microwave). The diffraction peaks of the reference Fe3O4 standard38,39 were well indexed with relative intensities, indicating the as-synthesized nanoparticles were the pure Fe3O4 phase and single-phase of the face-centered-cubic spinel. The magnetite phase was confirmed for both conventional and microwave treatments. However, differences in the average size of crystallites for Fe3O4 were observed, with sizes of 21 nm and 19 nm for the hydrothermal and microwave procedures, respectively. XRD diffraction peaks from anatase and magnetite were observed regardless of the treatment method used. It is worth noting that the size of the anatase crystallites is close to the reference material for the TiO2–Fe3O4 systems synthesized by conventional heating, but the use of microwave treatment leads to a decrease in the size of the anatase crystallites. When analyzing the determined phase compositions, it should be noted that the use of conventional heating leads to the assumed values. In the case of the microwave method, a smaller share of the anatase phase was observed in the TiO2–Fe3O4 systems. The observed differences in the phase systems are related to the kinetics of the conventional and microwave processes. The influence of the process kinetics on the final material is also apparent in the clear differences in the values of the lattice parameters compared to the literature. According to the data presented by Kubiak et al.37, the lattice parameters for anatase are a = 3.785 Å and c = 9.514 Å, and for magnetite, c = 8.396 Å. While the values obtained by us for magnetite are close to the literature, the increase in the a and b parameters in the case of the anatase was shown. The similarity of the ionic radical of Ti4+ (0.604 Å) and Fe3+ (0.645 Å) suggests the possibility of occupying some titanium dioxide lattice sites by iron ions40, leading to a reduction in the crystallinity of the final material, and an increase in the lattice parameters of the unit cell. Kamani et al.41 have also suggested that the reduction in crystallite size of Fe-doped materials compared to undoped nanoparticles may be related to the transfer of a small amount of Fe ions to the interstitial or TiO2 substitution site42. Additionally, it is worth noting that the increase in the a and b lattice parameters for anatase is particularly visible for materials synthesized by microwave processing, while there are no clear differences for materials obtained by conventional hydrothermal heating. This confirms the earlier observations of scientists that the high kinetics of the microwave process may result in disturbances in the crystal lattice, which ultimately may lead to the introduction of dopants ions.
The XRD patterns for TiO2–Fe3O4 systems synthesized by (a) hydrothermal and (b) microwave methods.
Raman spectroscopy was used to analyze TiO2–Fe3O4 systems, and the collected spectra are presented in Fig. 2. In the spectra for the reference samples H_TiO2 and M_TiO2, five characteristic bands were observed at 140 cm−1 (Eg), 195 cm−1 (Eg), 395 cm−1 (B1g), 520 cm−1 (B1g + A1g), and 640 cm−1 (Eg)43, corresponding to anatase. For samples H_Fe3O4 and M_Fe3O4, bands at 210 cm−1 (A1g), 271 cm−1 (Eg), and 385 cm−1 (Eg), as well as the band responsible for the 2nd-order scattering, confirming the magnetite structure44, were observed. By analyzing the Raman spectra for the TiO2–Fe3O4 systems, clear differences were observed between the results obtained for conventional and microwave treatments. For the samples of the H_TiO2–Fe3O4 series, peaks of the anatase structure were detected, while for magnetite structure, only a weak peak from 2nd-order scattering was observed. The absence of additional bands from magnetite may be due to the high intensity of bands characteristic of TiO2. In the case of the M_TiO2–Fe3O4 series, strong symmetry bands Eg, B1g, and B1g + A1g were found, indicating the anatase crystal structure. Additionally, as in the case of materials obtained using conventional processing, bands from 2nd-order scattering were noted. However, attention should be paid to the higher intensity of the mentioned band for the M_TiO2–Fe3O4 series. Furthermore, it should be noted that for materials synthesized using the microwave treatment, a shift of the peak towards higher wavenumbers is observed. Therefore, the location of the Eg band (143 cm−1) and its full width at half maximum (FWHM) were analyzed depending on the Fe3O4 weight ratio, and the obtained data are presented in Fig. 3.
The Raman spectra for TiO2–Fe3O4 systems synthesized by (a) hydrothermal and (b) microwave methods.
Raman spectra in the wavenumber range of 100–200 cm−1 for TiO2–Fe3O4 systems synthesized using (a) conventional and (b) microwave treatment, in particular the position of the anatase band Eg (143 cm−1) and FWHM Eg (143 cm−1) depending on wt% Fe3O4.
Based on the analyzed Raman spectra in the wavenumber range of 100–200 cm−1, it was confirmed that for TiO2–Fe3O4 materials fabricated using conventional processing, no significant changes in the position of the anatase Eg peak (143 cm−1) were noted. This confirms previous observations that anatase and magnetite coexist as two separate phases in the resulting systems. On the other hand, for materials obtained using the microwave process, a shift of the Eg band (143 cm−1) and its half-width towards higher values of the wavenumber was observed. It is worth noting that this relationship is linear up to the limit value of 10 wt% Fe3O4. Raman spectroscopy is highly sensitive to changes in molecules and is often used as a probe to determine the local structural properties of nanopowders12,45. Hardwick et al.46 have reported that the insertion of Li ions into anatase-type nanocrystalline TiO2 deforms the anatase tetragonal lattice, transforming it into an orthorhombic structure that creates new Raman active modes. Palomino-Merino et al.47 reported that in Er-doped TiO2 material, erbium induces a slight structural deformation that causes the origin of an anatase peak Eg (143 cm−1) to redshift. The main reason for the mentioned shift is the insertion of the Er ions into the TiO2 lattice. Based on the analysis of the Raman spectra, it can be inferred that the observed red shift in the M_TiO2–Fe3O4 sample series is likely a result of the incorporation of Fe ions into the TiO2 lattice. The effective incorporation of iron into the titanium dioxide lattice appears to occur up to a content of 10 wt% Fe3O4. However, for higher contents of iron (II, III) oxide, a blue shift in the Raman spectrum is observed. This could be due to a reduced number of sites in the TiO2 lattice where iron can be incorporated, resulting from a decrease in its concentration.
TEM and EDX analyses were carried out to characterize the morphology of the obtained materials in terms of particle shape and size. The images obtained in Fig. 4 reveal that nanoparticles of varying shapes, such as spherical, cubic, and octahedral, were observed in all the analyzed materials. The dimensions of the nanoparticles were dependent on the treatment method used. For instance, the conventional processing method resulted in particles with an average size of 25–50 nm, while the microwave method produced smaller nanoparticles with an average size of 10–20 nm. It is worth noting that the obtained materials exhibit a high tendency to aggregate nanoparticles regardless of the treatment method used, which is confirmed by the BET results (refer to Table S3 in the Supplementary Materials). This observation is consistent with previous studies, such as Belousov et al.48, who reported that microwave radiation could be used to not only expedite the synthesis of particles but also obtain more uniform materials compared to conventional heating.
From left: TEM, STEM images, and EDX maps for TiO2–Fe3O4 systems synthesized using conventional and microwave treatment.
EDX elemental mapping shown in Fig. 4 (The table containing information on the elemental composition is included in the Supplementary Materials—Table S4) indicates that the distribution of titanium and iron in the H_TiO2–Fe3O4 series is not uniform, with a high aggregation of nanoparticles into larger structures with a diameter of approximately 500 nm. Iron is primarily located in these nanoparticle aggregates. The aggregation process may be attributed to the long conventional treatment time, which is based on the collision of molecules and heat conduction mechanisms. In turn, the TiO2–Fe3O4 systems prepared using the microwave method exhibited a more homogeneous distribution of elements (except for sample M_2.5%Fe3O4) compared to the previously described samples. Additionally, as the content of Fe3O4 in the M_TiO2–Fe3O4 series increased gradually to 20 wt%, the presence of larger aggregates could be observed.
All results of magnetic measurements of synthesized TiO2–Fe3O4 systems are collected in Fig. 5. As inferred, the TiO2–Fe3O4 systems show similar magnetic properties as pure nano-Fe3O4. The temperature dependence of magnetization (Fig. 4c,d) shows a strong bifurcation of the Zero-Field-Cooling (ZFC) curve and Field-Cooled (FC) curve. For all the analyzed materials, no Verwey transition was observed, which is related to the small size of the magnetite nanoparticles49. On the other hand, for the curve measured during cooling in zero magnetic fields (ZFC), a clear broad maximum (~ 115 K) is seen, which is related to the blocking temperature (TB) of the magnetic nanoparticles50. The samples containing 10 and 15 wt% Fe3O4 show a clear broad maximum for the ZFC curve (at ~ 50 K and ~ 90 K, respectively), which is invisible for samples with low magnetite content (2.5% and 5 wt% Fe3O4). For the above-mentioned materials, no splitting of the ZFC and FC curves was observed either. This indicates a different size of magnetite nanoparticles in the analyzed materials—which is consistent with the previously presented XRD analysis51. In the case of magnetization curves (M(H)) measured at 300 K, we do not observe large differences between samples with different percentages of Fe3O4. Regardless of the analyzed material, no remanence or magnetic hysteresis was observed. It should be noted that the materials obtained using microwave treatment have higher magnetization values compared to the products of conventional processing. This is mainly due to the differences in the size of the crystallites and the content of the magnetite phase in the analyzed materials. Nevertheless, the obtained results suggest superparamagnetic properties for all obtained TiO2–Fe3O4 systems synthesized using the conventional and microwave pathways.
Magnetic properties of TiO2–Fe3O4 systems synthesized using (a,c) microwave and (b,d) conventional treatment: (a,b) dependence of magnetization on temperature for all tested samples measured in a constant magnetic field μ0H = 0.1 T with zoom-in of the low-field region, and (c,d) magnetization as a function of external magnetic field for oxide systems measured at T = 300 K.
Diffuse reflectance spectroscopy (DRS) was applied to explore the electronic states of the fabricated systems. Detailed Tauc plots on the basis of which the bandgap energy values were determined are included in the Supplementary Materials (see Fig. S2). The UV–vis spectra of the prepared nanocomposites are shown in Fig. 6. As Fig. 6a,b display, the absorption edge of H_TiO2 and M_TiO2 is ca. 385 nm, which correlates with pure anatase52,53. Regardless of the analyzed series of TiO2–Fe3O4 systems (H or M), a red shift of the absorption band edge was observed. This increase in absorption is believed to be due to a charge-transfer transition between the electrons of the iron oxide nanoparticles and the conduction band (or valence band) of TiO254, resulting in a redshift. The presence of iron oxide nanoparticles is also thought to increase the energy spacing of the TiO2 conduction band and lead to the quantization of TiO2 energy levels55,56, allowing for the absorption of the tailor-made LED light. However, it should also be noted that there are clear differences between materials obtained using conventional and microwave processing. In the case of samples fabricated using conventional processing, a significant reduction in the bandgap energy was noted, which may be due to the entrapment of TiO2 and Fe3O4 nanoparticles in the aggregates visible in STEM images, resulting in a deterioration of the absorption properties. On the other hand, for the microwave method, a narrow distribution of nanoparticles and no tendency to agglomerate was observed. Additionally, a shift in the Raman spectrum was confirmed for these materials, which may be associated with the introduction of iron into the TiO2 crystal lattice. These findings imply that the fabrication of TiO2–Fe3O4 via microwave pathways obtains a photocatalyst that can work under tailor-made light.
The DRS spectra for TiO2–Fe3O4 systems synthesized by (a) conventional hydrothermal and (b) microwave methods.
Photocatalytic degradation of metronidazole (20 mg/L) was carried out using a dosage of photocatalysts (1 g/L) and the results are shown in Fig. 7. The amount of the photocatalyst used were selected based on other scientific reports related to the photo-oxidation of metronidazole. Neghi et al.57 published a study using a dose of 2.5 g/L TiO2 which resulted in the full degradation of metronidazole (0.1 mg/L). In another report, Neghi et al.58 applied a lower photocatalyst dosage (0.3 g/L) for the degradation of 10 mg/L MNZ solution and observed 18% degradation after 120 min indicating lower dosage was not effective for the removal of metronidazole for a short period experiment.
The results of MNZ photodegradation using TiO2–Fe3O4 systems synthesized by (a) conventional hydrothermal and (b) microwave methods.
Figure 7a shows the photooxidation efficiency of metronidazole using TiO2–Fe3O4 photocatalysts synthesized via conventional hydrothermal treatment. Based on the results, the adsorption of MNZ on the surface of TiO2–Fe3O4 systems was in the range of 6–8% after 30 min. The photocatalytic degradation using mentioned systems showed better results only for the H_2.5%Fe3O4. Based on the findings, the removal efficiency of MNZ was near 90%, while for the reference H_TiO2 was approx. 80%. The further increase in the magnetite add-on resulted in a significant decrease in the efficiency of the photocatalytic activity. For the H_20% Fe3O4 sample, only 20% of the MNZ removal efficiency was obtained. The main reason for the decrease in photodegradation efficiency is the previously described change in the band gap energy. The increase in the content of Fe3O4 in the case of materials obtained using conventional processing was associated with the deterioration of the optical properties of these materials. In addition, the morphology, i.e. aggregates of nanoparticles with a size of nearly 500 nm, may promote the higher recombination rate of charge carriers59. On the other hand, photocatalytic degradation catalyzed by TiO2–Fe3O4 fabricated by microwave process (Fig. 7b) showed better results for samples containing 2.5% and 5 wt% Fe3O4. The removal efficiency of MNZ was 96% (M_2.5%Fe3O4) and 85% (M_5%Fe3O4), that significantly was higher than the removal efficiencies of M_TiO2 (80%) after 180 min of UV-LED irradiation.
Photoluminescence spectroscopy was utilized to comprehensively analyze the photocatalytic performance of the synthesized TiO2–Fe3O4 materials (see Fig. S3 in Supplementary Materials). The results showed a luminescence band close to ~ 450 nm, which is characteristic of bare TiO2. However, in the case of materials containing 2.5 and 5 wt% Fe3O4, there was a quenching of the luminescence, indicating suppression of the recombination of photogenerated holes and electrons in the TiO2–Fe3O4 systems. This can be attributed to the fact that excited electrons from the valence band of titanium dioxide pass to the conduction band and subsequently to the Fe3O4 structure. The increase in Fe3O4 content also caused quenching of the luminescence compared to bare TiO2, but an increase compared to materials containing lower Fe3O4 content. This may be due to the shielding effect of Fe3O4, as mentioned in previous studies by Cheng et al.60 and Stefan et al.61. However, a high content of Fe3O4 can act as an electron trap, leading to a reduction in the charge transfer between TiO2 and the photocatalytically active substrate, thereby limiting the photocatalytic performance of TiO2. The lower luminescence of materials obtained in the microwave process may indicate a greater ordering of the structure and the absence of recombination centers. Nevertheless, in both analyzed cases, the formation of TiO2–Fe3O4 systems leads to the quenching of luminescence, which has a key impact on the improvement of photocatalytic activity in the metronidazole removal process.
In order to gain a deeper understanding of the degradation mechanism in the presence of TiO2–Fe3O4 photocatalysts, we introduced scavengers capable of capturing photogenerated electrons, holes, and primary reactive oxygen species, such as hydroxyl radicals (*OH) and superoxide radical anions (*O2−), into the metronidazole solution. The obtained results were collected and presented in Fig. S4 in Supplementary Materials. The introduction of ammonium oxalate and silver nitrate as scavengers for electrons and holes resulted in a slight decrease of approximately 10% in the photooxidation efficiency of metronidazole (MNZ). This suggests that the recombination of charge carriers (electrons and holes) does not have a significant impact on the overall photo-oxidation efficiency, as confirmed by the analysis of photoluminescence spectra. On the other hand, the addition of tert-butanol as a scavenger for hydroxyl radicals (*OH) had a significant effect, reducing the photodegradation efficiency by approximately 50% for the analyzed materials. This indicates that *OH is an active species involved in the photooxidation process. Furthermore, the scavenging of superoxide radical anions (*O2−) had a considerable impact on the efficiency of MNZ removal, resulting in a decrease of approximately 60%. This highlights the crucial role played by *O2− in the photocatalytic degradation mechanism. Based on these observations, it can be inferred that the mechanisms occurring in aquatic environments are primarily governed by the generation of reactive oxygen species (ROS), including hydroxyl radicals and superoxide radical anions.
Another factor determining the improvement of MNZ removal efficiency in the case of materials obtained by the microwave method is the possibility of creating a heterojunction between the system components—TiO2 and Fe3O462,63. Based on the previously described Raman data, it was indicated that the possibility of introduction of Fe ions into the TiO2 lattice during microwave processing. In addition, these materials are characterized by smaller particle sizes and do not tend to agglomerate, which may improve optical properties by not trapping TiO2 in Fe3O4 aggregates. On this basis, a mechanism based on type I heterojunction was proposed64. The Fe3O4 conduction band is below the TiO2 conduction band, while the Fe3O4 valence band is above the TiO2 valence band. Because electrons and holes gain energy by moving down and up, respectively. Photoexcited electrons can transfer from the conduction band of TiO2 to the conduction band of Fe3O4, while holes can be transferred from the valence band of TiO2 to the valence band of Fe3O4 when there is sufficient contact between both semiconductors. In this way, all charge carriers accumulate on Fe3O4. The disadvantage of the proposed mechanism is that both electrons and holes accumulate on the same semiconductor, thus electron–hole pairs cannot be separated efficiently65. However, many scientific reports report that the type I heterojunction makes it possible to improve the photoactivity of the final material. Among others, Monitz et al.66 indicated that the TiO2(P25)–CuO material may be characterized by the higher efficiency of photocatalytic processes compared to the reference material. Figure 8 illustrates the proposed mechanism, which is consistent with the type I heterojunction.
Proposed mechanism of photooxidation of metronidazole using TiO2–Fe3O4 photocatalysts.
However, in the case of the synthesized TiO2–Fe3O4 systems, the improvement of photoactivity is the result of lowering the energy of the bandgap, which enabled higher absorption of radiation from the LED light source used. Moreover, Chu Chu et al.11 suggest that the anatase phase of TiO2 lattice in TiO2–Fe3O4 systems displays characteristics of a type I heterojunction mechanism. Hence, the surface of anatase can generate hydroxyl radicals that react with pollutants and enhance the efficiency of pollutant degradation. The substitution of titanium with iron ions in the TiO2 unit cell can increase the formation of lattice vacancies, leading to higher adsorption of surface water and the generation of more hydroxyl radicals67. Iron ions, particularly Fe3+, act as acceptors of photo-induced charge from the valence band of anatase, preventing the recombination of photo-induced charge by accepting photo-induced electrons. Fe2+, with one more electron than half-occupied 3d, can easily donate its redundant electron to surface-absorbed oxygen, leading to the generation of the superoxide anion10. Additionally, Fe3+ can accept photo-induced h+ and oxidize to Fe4+, which can react with surface hydroxide ions to produce surface hydroxyl radicals or recombine with photo-induced electrons68,69. The superior photocatalytic performance of TiO2–Fe3O4 systems is attributed to both the reduced bandgap and the quenching of the emission, indicating a lower recombination rate of charge carriers.
Thermogravimetric analysis (TGA) was conducted to confirm the exceptional stability of the synthesized materials (refer to Fig. S5 in the Supplementary Materials). TGA analysis was performed on the most efficient photocatalysts, and the results showed that the TiO2–Fe3O4 catalysts demonstrated high thermal resistance regardless of the synthesis method utilized (conventional hydrothermal or microwave process). The materials exhibited a mass loss of just over 3% up to 1000 °C.
The H_2.5%Fe3O4 and M_2.5%Fe3O4 photocatalysts were selected for the reusability test. The five subsequent cycles of MZN degradation were performed to study the photocatalytic reusability, as presented in Fig. S6 in Supplementary Materials. At each run’s end, the TiO2–Fe3O4 photocatalyst was separated using an external magnetic field. At the end of each cycle, the photocatalyst was removed from the degraded solution and transferred to the next photoreactor. The photocatalyst was not subjected to any additional treatment between catalytic cycles. The efficiency of photocatalytic degradation was maintained without a significant decline, even in the 5th cycle.
The photocatalytic system must be able to remove contaminants efficiently. However, nowadays, the economy of this process, and in particular its energy consumption, is extremely important. Therefore, taking into account the available scientific reports for the photocatalysts H_2.5%Fe3O4 and M_2.5%Fe3O4, the electrical energy per order (EEO)70 parameter was determined. It is the energy required for achieving the chosen level of abatement, for a fixed volume of wastewater, which can be thus calculated through the following formula (Eq. 3). Values of EE0 not higher than 2.5 are considered suitable for practical applications.
where P is the lamp power (kW), k is the pseudo-first-order constant (min−1), V is the volume of the reactor, and t is irradiation time. From the EEO values, it was evident that the photocatalytic system with TiO2–Fe3O4 photocatalyst and UV-LED light source was highly energy efficient. For analyzed samples, the mentioned parameter was 0.387 kWh m−3 order−1 for H_2.5%Fe3O4 and 0.308 kWh m−3 order−1 for M_2.5%Fe3O4. When comparing these values with similar photocatalytic systems used for metronidazole degradation, it should be noted that these values are lower than those reported by Pan et al.71. This fact confirms that tailor-made LED photocatalytic systems may in the future be used as part of wastewater treatment technology.
This study aimed to compare the conventional and microwave treatment methods for synthesizing TiO2–Fe3O4 photocatalyst used for metronidazole decomposition. The XRD results suggested that the reduction in crystallite size of Fe-doped materials compared to undoped nanoparticles may be related to the transfer of a small amount of Fe ions to the interstitial or TiO2 substitution site. The Raman spectra analysis revealed a shift of Eg band (143 cm−1) towards higher wavenumbers in the materials synthesized using the microwave process. This shift is likely the result of the incorporation of Fe ions into the TiO2 lattice. All synthesized systems show superparamagnetic properties and no Verwey transition or magnetic hysteresis was observed. However, the materials obtained using microwave treatment have higher magnetization values than those obtained using conventional processing. The DRS spectra showed a red shift of the absorption band edge and lower bandgap energy in all systems, which is related to the charge transfer transition between the electrons of the Fe3O4 nanoparticles and TiO2. The enhanced photoactivity is attributed to the possibility of creating a heterojunction between TiO2 and Fe3O4, leading to the accumulation of all charge carriers on Fe3O4. This approach enables the production of tailor-made photocatalytic systems where the photocatalyst and light source are spectrally matched.
The data that support the findings of this research are available from the corresponding author upon reasonable request.
Kougias, I., Taylor, N., Kakoulaki, G. & Jäger-Waldau, A. The role of photovoltaics for the European Green Deal and the recovery plan. Renew. Sustain. Energy Rev. 144, 111017 (2021).
Fetting, C. The European Green Deal (red. ESDN Office), 5-22, ESDN Report, 2020.
Eckert, E. & Kovalevska, O. Sustainability in the European Union: Analyzing the discourse of the European Green Deal. J. Risk Financ. Manag. 14, 80 (2021).
Montanarella, L. & Panagos, P. The relevance of sustainable soil management within the European Green Deal. Land Use Policy 100, 104950 (2021).
Teixeira, A. R. F. A. et al. Understanding the photocatalytic activity of sodium hexatitanate nanoparticles for pollutants degradation: A spectroscopic insight. ACS Appl. Nano Mater. 6, 4477–4488 (2022).
Zouheir, M. et al. Effective photocatalytic conversion of formic acid using iron, copper and sulphate doped TiO2. J. Cent. South. Univ. 29, 3592–3607 (2022).
Araujo, F. P. et al. New composite TiO2/naturals gums for high efficiency in photodiscoloration process. Ceram. Int. 46, 15534–15543 (2020).
Lopes, A. C. B. et al. TiO2/karaya composite for photoinactivation of bacteria. Materials 15, 4559 (2022).
Article ADS CAS PubMed PubMed Central Google Scholar
Tanji, K. et al. Epigrammatic progress on the photocatalytic properties of ZnO and TiO2 based hydroxyapatite@photocatlyst toward organic molecules photodegradation: A review. J. Water Process. Eng. 53, 103682 (2023).
Zhu, J., Chen, F., Zhang, J., Chen, H. & Anpo, M. Fe3+–TiO2 photocatalysts prepared by combining sol–gel method with hydrothermal treatment and their characterization. J. Photochem. Photobiol. A 180, 196–204 (2006).
Chu, A. C., Sahu, R. S., Chou, T. H. & Shih, Y. H. Magnetic Fe3O4@TiO2 nanocomposites to degrade bisphenol A, one emerging contaminant, under visible and long wavelength UV light irradiation. J. Environ. Chem. Eng. 9, 105539 (2021).
Guo, H. et al. A comprehensive insight into plasma-catalytic removal of antibiotic oxytetracycline based on graphene-TiO2–Fe3O4 nanocomposites. Chem. Eng. J. 425, 130614 (2021).
Fahoul, Y., Zouheir, M., Tanji, K. & Kherbeche, A. Synthesis of a novel ZnAl2O4/CuS nanocomposite and its characterization for photocatalytic degradation of acid red 1 under UV illumination. J. Alloys Compd. 889, 161708 (2021).
Tang, B. et al. Sol-solvothermal synthesis and microwave evolution of La(OH)3 nanorods to La2O3 nanorods. Nanotechnology 15, 1273–1276 (2004).
Article ADS CAS Google Scholar
Neville, E. M. et al. Carbon-doped TiO2 and carbon, tungsten-codoped TiO2 through sol–gel processes in the presence of melamine borate: Reflections through photocatalysis. J. Phys. Chem. C 116, 16511–16521 (2012).
Parashar, M., Shukla, V. K. & Singh, R. Metal oxides nanoparticles via sol–gel method: a review on synthesis, characterization and applications. J. Mater. Sci. Mater. Electron. 31, 3729–3749 (2020).
Livage, J. Sol–gel processes. Curr. Opin. Solid State Mater. Sci. 2, 132–138 (1997).
Article ADS CAS Google Scholar
Kubiak, A. et al. Controlled microwave-assisted and pH-affected growth of ZnO structures and their photocatalytic performance. Powder Technol. 386, 221–235 (2021).
Ng, H. K. M., Lim, G. K. & Leo, C. P. Comparison between hydrothermal and microwave-assisted synthesis of carbon dots from biowaste and chemical for heavy metal detection: A review. Microchem. J. 165, 106116 (2021).
Meng, L. Y., Wang, B., Ma, M. G. & Lin, K. L. The progress of microwave-assisted hydrothermal method in the synthesis of functional nanomaterials. Mater. Today Chem. 1–2, 63–83 (2016).
Chang, B. Y. S. et al. Hydrothermally prepared graphene-titania nanocomposite for the solar photocatalytic degradation of methylene blue. Desal. Water Treat. 57, 238–245 (2016).
Komarneni, S. & Roy, R. Titania gel spheres by a new sol–gel process. Mater. Lett. 3(4), 165–168 (1985).
Wang, H. E. et al. Microwave-assisted hydrothermal synthesis of porous SnO2 nanotubes and their lithium ion storage properties. J. Solid State Chem. 190, 104–110 (2012).
Article ADS CAS Google Scholar
Tsuji, M., Hashimoto, M., Nishizawa, Y., Kubokawa, M. & Tsuji, T. Microwave-assisted synthesis of metallic nanostructures in solution. Chem. Eur. J. 11, 440–452 (2005).
Article CAS PubMed Google Scholar
Jiang, H., Moon, K. S., Zhang, Z., Pothukuchi, S. & Wong, C. P. Variable frequency microwave synthesis of silver nanoparticles. J. Nanopart. Res. 8, 117–124 (2006).
Article ADS CAS Google Scholar
Puvvada, N. et al. Synthesis of biocompatible multicolor luminescent carbon dots for bioimaging applications. Sci. Technol. Adv. Mater. 13, 045008 (2012).
Article PubMed PubMed Central Google Scholar
Li, Y. & Yang, W. Microwave synthesis of zeolite membranes: A review. J. Membr. Sci. 316, 3–17 (2008).
Yang, Y. L., Hu, C. C. & Hua, C. C. Preparation and characterization of nanocrystalline TixSn1−xO2 solid solutions via a microwave-assisted hydrothermal synthesis process. CrystEngComm 13, 5638–5641 (2011).
Gedye, R. N., Smith, F. E. & Westaway, K. C. The rapid synthesis of organic compounds in microwave ovens. Can. J. Chem. 66, 17–23 (1988).
Moldovan, M. S. et al. On the evolution of Pt nanoparticles on few-layer graphene supports in the high-temperature range. J. Phys. Chem. C 116, 9274–9282 (2012).
Rai, P. et al. Microwave assisted hydrothermal synthesis of single crystalline ZnO nanorods for gas sensor application. Mater. Lett. 68, 90–93 (2012).
Zhu, Y. J. & Chen, F. Microwave-assisted preparation of inorganic nanostructures in liquid phase. Chem. Rev. 114, 6462–6555 (2014).
Article CAS PubMed Google Scholar
Kubiak, A. et al. Design and microwave-assisted synthesis of TiO2-lanthanides systems and evaluation of photocatalytic activity under UV-LED light irradiation. Catalysts 12, 8 (2022).
Rodríguez-Carvajal, J. Recent advances in magnetic structure determination by neutron powder diffraction. Phys. B Condens. 192, 55–69 (1993).
Dudziak, S. et al. Solvothermal growth of {0 0 1} exposed anatase nanosheets and their ability to mineralize organic pollutants. The effect of alcohol type and content on the nucleation and growth of TiO2 nanostructures. Appl. Surf. Sci. 563, 150360 (2021).
Zhu, C. L. et al. Fe3O4/TiO2 core/shell nanotubes: Synthesis and magnetic and electromagnetic wave absorption characteristics. J. Phys. Chem. C 114, 16229–16235 (2010).
Kubiak, A. et al. Hydrothermally assisted fabrication of TiO2–Fe3O4 composite materials and their antibacterial activity. Materials 13, 4715 (2020).
Article ADS CAS PubMed PubMed Central Google Scholar
Jędrzak, A., Rębiś, T., Kuznowicz, M. & Jesionowski, T. Bio-inspired magnetite/lignin/polydopamine-glucose oxidase biosensing nanoplatform. From synthesis, via sensing assays to comparison with others glucose testing techniques. Int. J. Biol. Macromol. 127, 677–682 (2019).
Jędrzak, A. et al. Polydopamine grafted on an advanced Fe3O4/lignin hybrid material and its evaluation in biosensing. Appl. Surf. Sci. 455, 455–464 (2018).
Carriazo, J. G., Moreno-Forero, M., Molina, R. A. & Moreno, S. Incorporation of titanium and titanium-iron species inside a smectite-type mineral for photocatalysis. Appl. Clay Sci. 50, 401–408 (2010).
Kamani, H., Ashrafi, S. D., Jahantiq, A., Norabadi, E. & Zadeh, M. D. Catalytic degradation of humic acid using Fe doped TiO2 ultrasound hybrid system from aqueous solution. J. Environ. Anal. Chem. 19, 79535 (2021).
Kronawitter, C. X. et al. Titanium incorporation into hematite photoelectrodes: Theoretical considerations and experimental observations. Energy Environ. Sci. 7, 3100–3121 (2014).
Perevedentseva, E. et al. Raman spectroscopic study of TiO2 nanoparticles’ effects on the hemoglobin state in individual red blood cells. Materials 14, 5920 (2021).
Article ADS CAS PubMed PubMed Central Google Scholar
Shebanova, O. N. & Lazor, P. Raman study of magnetite (Fe3O4): Laser-induced thermal effects and oxidation. J. Raman Spectrosc. 34, 845–852 (2003).
Article ADS CAS Google Scholar
Li, W. S., Shen, Z. X., Li, H. Y., Shen, D. Z. & Fan, X. W. Blue shift of Raman peak from coated TiO2 nanoparticles. J. Raman Spectrosc. 32, 862–865 (2001).
Hardwick, L. J., Holzapfel, M., Novák, P., Dupont, L. & Baudrin, E. Electrochemical lithium insertion into anatase-type TiO2: An in situ Raman microscopy investigation. Electrochim. Acta 52, 5357–5367 (2007).
Palomino-Merino, R. et al. Red shifts of the Eg(1) Raman mode of nanocrystalline TiO2: Er monoliths grown by sol–gel process. Opt. Mater. 46, 345–349 (2015).
Article ADS CAS Google Scholar
Belousov, O. V. et al. Formation of bimetallic Au–Pd and Au–Pt nanoparticles under hydrothermal conditions and microwave irradiation. Langmuir 27, 11697–11703 (2011).
Article CAS PubMed Google Scholar
Qiang, C. et al. Magnetic properties and microwave absorption properties of carbon fibers coated by Fe3O4 nanoparticles. J. Alloys Compd. 506, 93–97 (2010).
Xu, J. S. & Zhu, Y. J. γ-Fe2O3 and Fe3O4 magnetic hierarchically nanostructured hollow microspheres: Preparation, formation mechanism, magnetic property, and application in water treatment. J. Colloid. Interface Sci. 385, 58–65 (2012).
Article ADS CAS PubMed Google Scholar
Wei, Y. et al. Synthesis of Fe3O4 nanoparticles and their magnetic properties. Procedia Eng. 27, 632–637 (2012).
Jiang, W. L. et al. A novel TiO2/graphite felt photoanode assisted electro-Fenton catalytic membrane process for sequential degradation of antibiotic florfenicol and elimination of its antibacterial activity. Chem. Eng. J. 391, 123503 (2020).
Zhang, Y. et al. C-doped hollow TiO2 spheres: In situ synthesis, controlled shell thickness, and superior visible-light photocatalytic activity. Appl. Catal. B 165, 715–722 (2015).
Gholamian, S., Hamzehloo, M. & Farrokhnia, A. Enhanced visible-light photocatalysis of TiO2/Fe3O4/BiOI nanocomposites as magnetically recoverable for the degradation of dye pollutants. J. Environ. Chem. Eng. 9, 104937 (2021).
Nadimi, M., Ziarati Saravani, A., Aroon, M. A. & Ebrahimian Pirbazari, A. Photodegradation of methylene blue by a ternary magnetic TiO2/Fe3O4/graphene oxide nanocomposite under visible light. Mater. Chem. Phys. 225, 464–474 (2019).
Li, Z. Q., Wang, H. L., Zi, L. Y., Zhang, J. J. & Zhang, Y. S. Preparation and photocatalytic performance of magnetic TiO2–Fe3O4/graphene (RGO) composites under VIS-light irradiation. Ceram. Int. 41, 10634–10643 (2015).
Neghi, N., Kumar, M. & Burkhalov, D. Synthesis and application of stable, reusable TiO2 polymeric composites for photocatalytic removal of metronidazole: Removal kinetics and density functional analysis. Chem. Eng. J. 359, 963–975 (2019).
Neghi, N., Krishnan, N. R. & Kumar, M. Analysis of metronidazole removal and micro-toxicity in photolytic systems: Effects of persulfate dosage, anions and reactor operation-mode. J. Environ. Chem. Eng. 6, 754–761 (2018).
Li, H. et al. Architecturing CoTiO3 overlayer on nanosheets-assembled hierarchical TiO2 nanospheres as a highly active and robust catalyst for peroxymonosulfate activation and metronidazole degradation. Chem. Eng. J. 392, 123819 (2020).
Cheng, H. et al. Synergetic effect of Fe3O4 nanoparticles and carbon on flexible poly(vinylidence fluoride) based films with higher heat dissipation to improve electromagnetic shielding. Compos. Part. A Appl. Sci. Manuf. 121, 139–148 (2019).
Stefan, M. et al. Magnetic recoverable Fe3O4–TiO2: Eu composite nanoparticles with enhanced photocatalytic activity. Appl. Surf. Sci. 390, 248–259 (2016).
Article ADS CAS Google Scholar
Ensafi, A. A., Nasr-Esfahani, P. & Rezaei, B. Metronidazole determination with an extremely sensitive and selective electrochemical sensor based on graphene nanoplatelets and molecularly imprinted polymers on graphene quantum dots. Sens. Actuators B Chem. 270, 192–199 (2018).
Sheikhmohammadi, A., Asgari, E., Nourmoradi, H., Fazli, M. M. & Yeganeh, M. Ultrasound-assisted decomposition of metronidazole by synthesized TiO2/Fe3O4 nanocatalyst: Influencing factors and mechanisms. J. Environ. Chem. Eng. 9, 105844 (2021).
Lopis, A. D. et al. Laddered type-1 heterojunction: Harvesting full-solar-spectrum in scavenger free photocatalysis. Sol. Energy 240, 57–68 (2022).
Article ADS CAS Google Scholar
Ding, J. et al. Boosted interfacial polarization from multishell TiO2@Fe3O4@PPy heterojunction for enhanced microwave absorption. Small 15, 1902885 (2019).
Moniz, S. J. A. & Tang, J. Charge transfer and photocatalytic activity in CuO/TiO2 nanoparticle heterojunctions synthesised through a rapid, one-pot, microwave solvothermal route. ChemCatChem 7, 1659–1667 (2015).
Adán, C., Bahamonde, A., Fernández-García, M. & Martínez-Arias, A. Structure and activity of nanosized iron-doped anatase TiO2 catalysts for phenol photocatalytic degradation. Appl. Catal. B 72, 11–17 (2007).
Hung, W. C., Chen, Y. C., Chu, H. & Tseng, T. K. Synthesis and characterization of TiO2 and Fe/TiO2 nanoparticles and their performance for photocatalytic degradation of 1,2-dichloroethane. Appl. Surf. Sci. 255, 2205–2213 (2008).
Article ADS CAS Google Scholar
Yalçin, Y., Kiliç, M. & Çinar, Z. Fe+3-doped TiO2: A combined experimental and computational approach to the evaluation of visible light activity. Appl. Catal. B 99, 469–477 (2010).
Neghi, N. & Kumar, M. Performance analysis of photolytic, photocatalytic, and adsorption systems in the degradation of metronidazole on the perspective of removal rate and energy consumption. Water Air Soil Pollut. 228, 339 (2017).
Pan, Y., Li, X., Fu, K., Deng, H. & Shi, J. Degradation of metronidazole by UV/chlorine treatment: Efficiency, mechanism, pathways and DBPs formation. Chemosphere 224, 228–236 (2019).
Article ADS CAS PubMed Google Scholar
This work was funded by the National Science Centre of Poland (2021/43/D/ST5/01190).
Faculty of Chemistry, Adam Mickiewicz University, Uniwersytet Poznanskiego 8, 61614, Poznan, Poland
You can also search for this author in PubMed Google Scholar
A.K.: Conceptualization, Methodology, Formal analysis, Investigation, Data curation, Resource, Visualization, Writing—Original Draft; Writing—Review & Editing, Funding acquisition.
The author declares no competing interests.
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
Kubiak, A. Comparative study of TiO2–Fe3O4 photocatalysts synthesized by conventional and microwave methods for metronidazole removal. Sci Rep 13, 12075 (2023). https://doi.org/10.1038/s41598-023-39342-9
DOI: https://doi.org/10.1038/s41598-023-39342-9
Anyone you share the following link with will be able to read this content:
Sorry, a shareable link is not currently available for this article.
Provided by the Springer Nature SharedIt content-sharing initiative
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.
Scientific Reports (Sci Rep) ISSN 2045-2322 (online)
Lithopone And Titanium Dioxide Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.